Jade Flow Singapore: Biker Shorts Built on Modal/Spandex French Terry
Jade Flow, based in Singapore, needed a biker shorts that delivered fast drying after heavy use without moving away from a clean, commercial silhouette. The finished fabric was Modal/Spandex French Terry.
Project brief and fabric selection
The fabric selected combines French Terry (looped back construction) with cellulosic fibre with elastane, giving soft drape and high comfort. Construction is looped back construction at 240-300 GSM. The brief also asked for plus a soft loop length. Each lot was checked against AATCC 199 drying rate before cutting began.
Construction and fit decisions
Pattern and construction were adjusted around the chosen fabric: seam placement moved away from high-friction areas, stitch density was matched to the elastane content, and the fit block was revised once the first wear trial showed the panel tension distribution. The development brief set the outcome as the garment dried in 24 minutes under test conditions.
Dyeing and finishing approach
Finishing was limited to processes that support fast drying after heavy use. Soft handle came from construction rather than heavy softening, which keeps performance stable through repeated washing. Consistency between repeat lots mattered more to Jade Flow than an isolated best result.
Measured results
Measured outcome: the garment dried in 24 minutes under test conditions, verified by AATCC 199 drying rate. Size sets were checked after five home washes to confirm that dimensional change stayed inside the agreed tolerance before bulk release. Fabric Modal/Spandex French Terry supplied the base behaviour for fast drying after heavy use.
Repeat order performance
The style moved to repeat orders after two seasons. Bulk fabric is now booked against a fixed recipe, with test reports issued per lot, and the French Terry construction is used for additional colourways in the same programme. The Singapore market requires documentation, so reports shipped with every lot.